We adopt high quality low-carbon steel rod to process hot-dip galvanized iron wires. It gets through the process of the low carbon steel after drawing molding, pickling derusting, high temperature annealing and galvanized.
The steel galvanized wire is distributed into the hot-dip galvanized wire and cold electricity galvanized wire. Compared with electro galvanized steel wires, the hot dipped wire has distinction for many aspects. The heated hot galvanizing is melting liquid zinc plating, soak in producing speed, whose coating thickness is uneven.
The minimum thickness market permits 45 micron and tiptop is more than 300 microns. Thanks to the Darker color, consumption, the base zinc metal metal forming infiltration layer and corrosion resistance, outdoor environment galvanized can keep decades.
The hot-dip galvanized iron wire is in electroplating slot through the current mono-direction make zinc plating appearance, and production speed of the metal is gradually slow. Coating thickness of uniform is relatively thinner, and usually only 3-15 microns, whose appearance of brightness, corrosion resistance is poor with generally months being rust.
Production Process of Hot Dipped Iron Wire: Steel rod coil -- Wire Drawing -- Wire Annealing -- Rust Removing--Acid Washing-- Boiling-- Drying-- Zinc Feeding-- Wire Coiling.
Features: Hot dipped galvanized iron wire has outstanding toughness and flexibility, which can achieve the highest amount of zinc 300 grams/square meters. It possesses galvanized layer thickness, strong corrosion resistance and other properties.
Applications: Hot-dip galvanized wire products are extensively utilized as binding wires in construction, handicrafts, wire mesh screens, highway guardrails, product packaging and daily civil, etc.